Structures by: Shoemaker C. B.
Total: 17
Manganese yttrium deuteride (23/6/8.3)
D8.3Mn23Y6
Journal de Physique (Paris) (1979) 40, L639-L642
a=12.7853Å b=12.7853Å c=12.7853Å
α=90° β=90° γ=90°
Manganese yttrium deuteride (23/6/18)
D18Mn23Y6
Journal de Physique (Paris) (1979) 40, L639-L642
a=12.799Å b=12.799Å c=12.799Å
α=90° β=90° γ=90°
Manganese yttrium deuteride (23/6/23)
D23Mn23Y6
Journal de Physique (Paris) (1979) 40, L639-L642
a=12.84Å b=12.84Å c=12.84Å
α=90° β=90° γ=90°
Manganese yttrium deuteride (23/6/8.32)
D8.323Mn23Y6
Journal de Physique, Lettres (1979) 40, L639-L642
a=12.7853Å b=12.7853Å c=12.7853Å
α=90° β=90° γ=90°
Manganese yttrium deuteride (23/6/22.92)
D22.92Mn23Y6
Journal de Physique, Lettres (1979) 40, L639-L642
a=12.84Å b=12.84Å c=12.84Å
α=90° β=90° γ=90°
Manganese yttrium deuteride (23/6/18)
D18Mn23Y6
Journal de Physique, Lettres (1979) 40, L639-L642
a=12.799Å b=12.799Å c=12.799Å
α=90° β=90° γ=90°
Mn23Y6
Mn23Y6
Journal de Physique, Lettres (1979) 40, L639-L642
a=12.5063Å b=12.5063Å c=12.5063Å
α=90° β=90° γ=90°
Mn44.1Si8.9
Mn44.1Si8.9
Acta Crystallographica B (24,1968-38,1982) (1978) 34, 701-705
a=10.871Å b=10.871Å c=19.18Å
α=90° β=90° γ=120°
Mn5Si2
Mn5Si2
Acta Crystallographica B (24,1968-38,1982) (1976) 32, 2306-2313
a=8.9097Å b=8.9097Å c=8.7153Å
α=90° β=90° γ=90°
(Cr9 Mo21 Ni20)1.12
Cr10.08Mo23.52Ni22.4
Acta Crystallographica (1,1948-23,1967) (1955) 8, 734-735
a=17.01Å b=4.74Å c=9.07Å
α=90° β=90° γ=90°
Ti Ni Si
NiSiTi
Acta Crystallographica (1,1948-23,1967) (1965) 18, 900-905
a=6.1484Å b=7.0173Å c=3.6698Å
α=90° β=90° γ=90°
MoNi
MoNi
Acta Crystallographica (1,1948-23,1967) (1963) 16, 997-1009
a=9.108Å b=9.108Å c=8.852Å
α=90° β=90° γ=90°
Cr9.61Mo25.12Ni21.27
Cr9.61Mo25.12Ni21.27
Acta Crystallographica (1,1948-23,1967) (1955) 8, 734-735
a=9.07Å b=17.01Å c=4.74Å
α=90° β=90° γ=90°
Cr9.54Mo25.24Ni21.22
Cr9.54Mo25.24Ni21.22
Acta Crystallographica (1,1948-23,1967) (1957) 10, 1-14
a=16.983Å b=4.752Å c=9.07Å
α=90° β=90° γ=90°
Manganese-beta
Mn
Acta Crystallographica, Section B (1978) 34, 3573-3576
a=6.315Å b=6.315Å c=6.315Å
α=90° β=90° γ=90°
Mn3.28Ni1.01Si0.71
Mn3.28Ni1.01Si0.71
Acta Crystallographica, Section B (1978) 34, 3573-3576
a=6.292Å b=6.292Å c=6.292Å
α=90° β=90° γ=90°
Al2.26Nb0.8Ti2.94
Al2.26Nb0.8Ti2.94
Acta Crystallographica, Section C (1990) 46, 374-377
a=4.5554Å b=4.5554Å c=5.5415Å
α=90° β=90° γ=120°